Modèle:  1000series, 3000series, 5000series, 6000series

Description du produit

Numéro de modèle : 1000series, 3000series, 5000series, 6000series Certification : ASTM, JIS, GB/T Grade : 1000series, 3000series, 5000series, 6000series Traitement de surface : Mill Finish Échantillon : Forme libre : Rectangulaire Spécifications : SGS, ROHS Code HS : 760612 Application : Décorations, outils de transport, porte et fenêtre, mur de verre, dissipateur de chaleur Technique : laminage Tempérament : O - H112 Alliage : Alliage et non-alliage Type : Feuilles d'aluminium Marque : Baodi Origine : CHINE Spécification de la feuille d'aluminium comme ci-dessous :

Alliage : 1050, 1060, 1100, 1200, 1350, 3003, 3004, 3105, 5052, 5754, 5456, 5005, 5083, 5251, 6061, 6063, 6082, 7075
Temper : O, H14, H24, H18, H26, H22, T4, T6
Épaisseur : de 0,1 mm à 6 mm
Largeur : jusqu'à 1800 mm
Longueur : jusqu'à 6000 mm
Dimension : peut être personnalisé selon vos besoins.

Nous fournissons des processus et un service d'usinage tels que la coupe de feuilles en spécial taille, cercle coupé, triangle et autre forme, feuille de PVC enduite, anodisation, trou de perforation et ainsi de suite.

Specification Name: 5000 series Aluminum Sheet
Alloy: 5052, 5005, 5754, 5083 etc.
Temper: O, H12, H22, H32, H14, H24, H26, H18, H112 etc.
Thickness: 0.2-200mm
Width: Up to 1800mm
Length: up to 6000mm
Surface treatment: mill finished, PVC coated, Print marks
Feature Machinability: It has relatively fair machinability. It is easier to machine in the hard temper than as annealed and the quality of finish is better if machined in the hard condition. Oil lubricants should be used for machining, except that very light cuts may be done dry.
Forming: It is readily formed at room temperature. Successive cold working decreases the formability.
Heat Treatment: It cannot be hardened by means of heat treatment. It does harden due to cold working.
Forging: It may be forged in the temperature range of 950 F down to 500 F
Cold Working: The alloy cold works readily and may be formed by drawing or spinning. However the amount of cold work imparted by spinning makes intermediate annealing necessary.
Annealing: Anneal at 650 F and air cool.
Hardening: Hardens only from cold working.
Application hydraulic tubes, kitchen cabinets, small boats, home freezers, milk crates, aircraft tube, fencing, small boats, gas lines, refrigerator panels, utensils, welded pressure vessels, marine, auto aircraft cryogenics, drilling rigs, TV towers, transportation equipment, missile components etc.
Alloy Chemical Component %≤
Si Fe Cu Mn Mg Cr Ni Zn Ti others Al
single total
5052 0.25 0.4 0.1 0.1 2.2-2.8 0.15-0.3 \ 0.1 \ 0.05 0.15 remainder
5005 0.3 0.7 0.2 0.2 0.5-1.1 0.1 \ 0.25 \ 0.05 0.15 remainder
5754 0.4 0.4 0.1 0.5 2.6-3.6 0.3 \ 0.2 0.15 0.05 0.15 remainder
5083 0.4 0.4 0.1 0.4-1.0 4.0-4.9 0.05-0.25 \ 0.25 0.15 0.05 0.15 remainder
Contact Ms. Cherry Xia   Tel: 0086-0535-6879033

Aluminum Sheet From China Manufacturer
Aluminum Sheet From China Manufacturer
Aluminum Sheet From China Manufacturer

Groupes de Produits : Feuille d'aluminium

Envoyer à ce fournisseur
  • *Sujet:
  • pour:

  • *Messages:
    Votre message doit comporter de 20 à 8000 caractères