Plaque en aluminium trempé 6061 T6

Informations de base

Modèle:  6061

Description du produit

Numéro de modèle : 6061 Certification : ASTM, JIS, GB/T Grade : 6000 Series Traitement de surface : Mill Finish Certification 1 : ISO9001 : 2008 exporté vers 1 : plus de 20 pays tels que les États-Unis, le Royaume-Uni, l'Inde et le Brésil exportés vers 3 : Thaïlande , Indonésie, Malaisie, Iran, Egypte Stock : 5 millions de dollars Nouveau stock pour répondre à la livraison rapide Forme : Rectangulaire Spécification : SGS, ROHS Code HS : 760612 Application : Moule, Structure, Marine Technique : Trempé Etat : T3 - T8 Alliage : Alliage Certification 2: SGS-Cstc Qpi-Asi125075 exporté vers 2: Chili, Argentine, Pérou, Équateur, Yémen Exporté vers 4: Vietnam, Croatie, Belgique, Afrique du Sud, Italie Type: Plaque Marque: Baodi Origine: Chine ISO9001: 2008 certifié
SGS certifié\plus de 20 ans d'expérience professionnelle sur l'aluminium
Exporté dans plus de 20 pays

Alliage : 6061
Épaisseur : 0, T6
Épaisseur : 6.0-200mm
Largeur : au besoin

Longueur : au besoin
Souvent utilisé pour fabrication de moules.

L'alliage 6061 a de très bonnes caractéristiques de soudage et peut être soudé par tous les wel communs techniques de ding. Le soudage à l'arc au tungstène gazeux est généralement utilisé pour les sections minces et le soudage à l'arc au gaz métal est utilisé pour les sections plus lourdes.

Couramment utilisé dans la fabrication de structures lourdes nécessitant une bonne résistance à la corrosion, de composants de camions et marins, de wagons, de meubles, de réservoir raccords, applications structurelles générales et haute pression, produits en fil et dans les pipelines.

Specification Name: 6000 series Aluminum Sheet
Alloy: 6061, 6082, 6063 etc.
Temper: O, H112, T4, T6, T651 etc.
Thickness: 6-200mm
Width: Up to 1500mm
Surface treatment: mill finished, Print marks
Feature Machinability: In the harder T 4 and T6 tempers it is good. It is notably less easy to machine in the annealed temper.
Forming: Easily cold worked and formed in the annealed condition. Stamping, bending, spinning, deep drawing are all readily accomplished using standard methods.
Welding: It has very good welding characteristics and may be welded by all of the common welding techniques.
Heat Treatment: Solution heat treat at 990 F for adequate time to allow for thorough heating and then water quench. Precipitation hardening is done at 320 F for 18 hours and air cool, followed by 350 F for 8 hours and air cooling.
Forging: It is capable of being hot forged at temperatures in the range of 900 F to 750 F.
Hot Working: Hot working may be done in the temperature range of 700 F to 500 F.
Cold Working: Cold working in the O temper condition is readily performed. The alloy is notably less easy to cold form in the T 4 and T 6 tempers.
Annealing: Annealing should be done at 775 F for 2 to 3 hours followed by controlled cooling at 50 f per hour down to 500 F, then air cool.
Aging: The aging precipitation heat treatment is done at 350 F for 8 hours followed by air cooling. This produces the T6 temper.
Application Commonly used in the manufacture of heavy-duty structures requiring good corrosion resistance, truck and marine components, railroad cars, furniture, tank fittings, general structural and high pressure applications, wire products, pipelines, various toolings etc.
 
Alloy Chemical Component %≤
Si Fe Cu Mn Mg Cr Ni Zn Ti others Al
single total
6061 0.4- 0.8 0.7 0.15-0.4 0.15 0.8- 1.2 0.04-0.35 \ 0.25 0.15 0.05 0.15 remainder
6082 0.7- 1.3 0.5 0.1 0.4- 1.0 0.6- 1.2 0.25 \ 0.2 0.1 0.05 0.15 remainder
6063 0.2-
0.6
0.35 0.1 0.1 0.45-0.9 0.1 \ 0.1 0.1 0.05 0.15 remainder
Contact Ms. Cherry Xia   Tel: 0086-15106464366

Groupes de Produits : Feuille d'aluminium

Envoyer à ce fournisseur
  • *Sujet:
  • pour:

  • *Messages:
    Votre message doit comporter de 20 à 8000 caractères